Research on Corrosion Fatigue Crack Propagation Behavior of Welded Joints of A7N01P-T4 Aluminum Alloys

Article PDF

Research on Corrosion Fatigue Crack Propagation Behavior of Welded Joints of A7N01P-T4 Aluminum Alloys

J. Chen, J. Xu, M. Zhao, G. Gou

download PDF

Abstract: Corrosion fatigue crack propagation behavior of welded joints a of A7N01P-T4 aluminum alloys were investigated. The corrosion fatigue crack propagation rate of base metal is higher than that of the heat-affected zone and the welding seam has a better corrosion fatigue resistance.

Keywords
High Speed Train, Corrosion Fatigue, A7N01P-T4 Aluminum Alloy

Published online 12/22/2016, 4 pages
Copyright © 2016 by the author(s)
Published under license by Materials Research Forum LLC., Millersville PA, USA

Citation: J. Chen, J. Xu, M. Zhao, G. Gou, ‘Research on Corrosion Fatigue Crack Propagation Behavior of Welded Joints of A7N01P-T4 Aluminum Alloys’, Materials Research Proceedings, Vol. 2, pp 599-602, 2017

DOI: http://dx.doi.org/10.21741/9781945291173-101

The article was published as article 101 of the book Residual Stresses 2016

Content from this work may be used under the terms of the Creative Commons Attribution 3.0 licence. Any further distribution of this work must maintain attribution to the author(s) and the title of the work, journal citation and DOI.

References
[1] Lv Shengli, ZHANG youhong, LV guozhi.·research and evaluation on corrosion damage of aluminium alloy structure.Xian, Northwestern Polytechnic University Press, 2009.169.
[2] H. Seifert, S. Ritter, Corrosion Science 2016.
[3] GOU Guoqing,HUANG Nan,CHEN Hui,LI Da,MENG Lichun. Analysis on corrosion behavior of welded joint of A7N01S-T5 aluminum alloy for high-speed train. Transaction of the China Welding Institution. 2011,32(10):17-20.
[4] Frederic Menan, Gilbert Henaff. Influence of frequency and exposure to a saline solution on the corrosion fatigue crack propagation behavior of the aluminum alloy 2024[J]. Intenational Journal of Fatigue, 2009, 31: 1684-1695. http://dx.doi.org/10.1016/j.ijfatigue.2009.02.033
[5] U.Zupanca, J.Grumb. Effect of pitting corrosion on fatigue performance of shot-peened aluminium alloy 7075-T651[J]. Journal of Materials Processing Technology, 2010, 210: 1197-1202. http://dx.doi.org/10.1016/j.jmatprotec.2010.03.004
[6] ZHANG Zhenggui,ZHOU Zhaoyuan, LIU Changyong. Corrosion fatigue failure analysis of high-strength aluminum alloy[J].Journal of Chinese Society for Corrosion and Protection, 2008, 28(1): 48-51.